Sample Record for 2024-07-18-49

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 994889 DEA: 051M7304 EFIS: 0520000055 QA Service Level: 1
DIST-CO-RTE-PM: 05-SCR-17-3.2/11.3
Work Description: HIGH FRICTION SURFACE TREATMENT, COLD PLANE AND PLACE HMA.
Location Description: SANTA CRUZ COUNTY IN AND NEAR SCOTT VALLEY FROM SOUTH OF MT HERMON ROAD TO 0.6 MILE NORTH OF GLENWOOD DRIVE
Contractor Name: GRANITE ROCK COMPANY
Contractor Address: 350 Technology Drive, Watsonville, CA 95076
Resident Engineer: Farshad Keshavarzi Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2024-07-18-49
TL Number from the TL Form: Sacramento Caltrans lab
Sample Submitted By Organization: Kwik Bond Polymers
Sample Organization Contact: (760) 518-6064
Type of Sample: Quality Control
Type of Material: High Friction Surface Treatment
Sample Taken Date: 07/18/2024
Date that the sample was received by the laboratory/organization performing the testing: 07/19/2024
The quantity of what the sample constitutes: 34 Totes
A brief description of the sample: 1 gallon can / HFST RESIN
From where was the sample collected: Source
Laboratory sample identification: 000096KBP
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Kwik Bond Polymers, Benicia

Material Information

Mgf. Lot Number(s): AZ4G01045T
Batch Number: AZ4G01045T
Mix Number: AZ4G01045T
Resin Binder Type: Polyester
Used for Overlay: Yes
Used for Inlay: No
Test results on following page(s): 2

Test Results

Test 1 of 2

DIME Test ID: 2024-07-18-49-1
Test Method: ASTM D2196-Feb15: Standard Test Methods for Rheological Properties of Non-Newtonian Materials by Rotational Viscometer
Verified Date: 08/27/2024
Date Tested: 08/27/2024
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joe.harline@dot.ca.gov
Organization Phone: (916) 206-4373
General Comments for this Test: ASTM C881 (Gel time): 27 mins. ASTM D1640 (Cure rate): 1.25 hrs
Test Result Compliance: complies
Additional Comments When Verified:
Viscosity 2148

Test 2 of 2

DIME Test ID: 2024-07-18-49-2
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Verified Date: 08/27/2024
Date Tested: 07/25/2024
Submitted By Organization: CT HQ - Sacramento Concrete Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joe.harline@dot.ca.gov
Organization Phone: (916) 206-4373
General Comments for this Test: Accepted vendor's results.
Test Result Compliance: complies
Additional Comments When Verified:
Number of specimens tested 6
Conditioning procedure 18/25/50+5/70
Speed of testing 0.45 in/min
Sample 1 Width 0.137 in
Sample 1 Ultimate strength 3789 psi
Sample 1 Thickness 0.491 in
Sample 1 Area 0.0673 in^2
Sample 1 Ultimate Strength Actual 255 lbs
Sample 1 percent elongation 40 %
Sample 1 Time no data0 MM:SS
Sample 2 Width 0.138 in
Sample 2 Thickness 0.487 in
Sample 2 Area 0.0672 in^2
Sample 2 Ultimate strength 3943.5 psi
Sample 2 Ultimate Strength Actual 265 lbs
Sample 2 percent elongation 43 %
Sample 2 Time no data0 MM:SS
Sample 3 Width 0.15 in
Sample 3 Thickness 0.487 in
Sample 3 Area 0.0731 in^2
Sample 3 Ultimate strength 3994.5 psi
Sample 3 Ultimate Strength Actual 292 lbs
Sample 3 percent elongation 60 %
Sample 3 Time no data0 MM:SS
Sample 4 Width 0.139 in
Sample 4 Thickness 0.491 in
Sample 4 Area 0.0682 in^2
Sample 4 Ultimate strength 3944.3 psi
Sample 4 Ultimate Strength Actual 269 lbs
Sample 4 percent elongation 47 %
Sample 4 Time no data0 MM:SS
Sample 5 Width 0.147 in
Sample 5 Thickness 0.485 in
Sample 5 Area 0.0713 in^2
Sample 5 Ultimate strength 4039.3 psi
Sample 5 Ultimate Strength Actual 288 lbs
Sample 5 percent elongation 60 %
Sample 5 Time no data0 MM:SS
Sample 6 Width 0.146 in
Sample 6 Thickness 0.492 in
Sample 6 Area 0.0718 in^2
Sample 6 Ultimate strength 4011.1 psi
Sample 6 Ultimate Strength Actual 288 lbs
Sample 6 percent elongation 52 %
Sample 6 Time no data0 MM:SS
Ultimate Strength Average 3954 psi
Percent Elongation Average 50 %