Sample Information

DIME Sample ID: 2015-11-06-6
TL Number from the TL Form: Unknown
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (530) 329-6527
Type of Sample: Quality Assurance
Type of Material: SMTL TM1 - Elastomeric Bearing Pad
Sample Taken Date: 11/06/2015
Date that the sample was received by the laboratory/organization performing the testing: 11/09/2015
The quantity of what the sample constitutes: 1
A brief description of the sample: Bearing Pad
From where was the sample collected: Fabricator
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: scougal

Material Information

Mfg. Lot Number(s): NA
Material/Compound/Elastomer ID: RS 15 16050569
Samples Representing: 1
Description (size): .125in Roll Stock
Comments: Unknown
Description (Number of Shims): NA
Type of Bearing Pad: Plain
Description (Thickness of Shims): NA
Manufacturer(s): Scougal
Batch Number: NA
Test results on following page(s): 3

Test Results

Test 1 of 3

DIME Test ID: 2015-11-06-6-1
Test Method: ASTM D2240-05re10: Standard Test Method for Rubber Property - Durometer Hardness
Verified Date: 11/25/2015
Date Tested: 11/13/2015
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Temperature 72 f
Humidity 50 %
Reading #1 52
Reading #2 53
Reading #3 55
Reading #4 54
Reading #5 53
Mean 53.4

Test 2 of 3

DIME Test ID: 2015-11-06-6-2
Test Method: ASTM D412-06a-re13: Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers-Tension
Verified Date: 11/25/2015
Date Tested: 11/13/2015
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Number of specimens tested 3
Unit of the Ultimate Tensile Values lbf per sqr in
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.078 in
Sample 1 Thickness all Within 0.003 inch? Yes
Sample 1 Ultimate Tensile 2410.3 lbf/in^2
Sample 1 Elongation (350% Min) Pass
Sample 2 Median Thickness 0.078 in
Sample 2 Thickness all Within 0.003 inch? Yes
Sample 2 Ultimate Tensile 2410.3 lbf/in^2
Sample 2 Elongation (350% Min) Pass
Sample 3 Median Thickness 0.076 in
Sample 3 Thickness all Within 0.003 inch? Yes
Sample 3 Ultimate Tensile 2368.4 lbf/in^2
Sample 3 Elongation (350% Min) Pass
Median of the Ultimate Tensile Values 2410.3 lbf/in^2

Test 3 of 3

DIME Test ID: 2015-11-06-6-3
Test Method: ASTM D624-00-re12: Standard Test Method for Tear Strength of Conventional Vulcanized Rubber and Thermoplastic Elastomers
Verified Date: 11/25/2015
Date Tested: 11/13/2015
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Number of specimens tested 3
UTM 2KIP
Humidity 50 %
Temperature 72 F
Sample 1 Median Thickness 0.065 in
Sample 1 Tear Strength 215.4 lbf / in
Sample 2 Median Thickness 0.088 in
Sample 2 Tear Strength 227.3 lbf / in
Sample 3 Median Thickness 0.073 in
Sample 3 Tear Strength 191.8 lbf / in
Median of the Tear Strength Values 215.4 lb/in