Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 44444 DEA: ASCP EFIS: ASCP
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2022-12-19-27
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Department Acceptance
Type of Material: Asphalt Binder
Sample Taken Date: 12/19/2022
Date that the sample was received by the laboratory/organization performing the testing: 01/12/2023
The quantity of what the sample constitutes: 1can
A brief description of the sample: PG58-16 Asphalt binder
From where was the sample collected: Manufacturer
Laboratory sample identification: 5816221219
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: San Joaquin Refining Co Inc
Performance Grade: PG 58-16
Modified:
Lot number:
Sublot number:
Tank number: TK 2002
Time of sample:
HMA Supplier:
Certified Asphalt Supplier: San Joaquin Refinery - Bakersfield CA
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:
DIME Test ID: 2022-12-19-27-1
Test Method: AASHTO T315-22: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 01/17/2023
Date Tested: 01/12/2023
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: OG.
Test Result Compliance: complies
Additional Comments When Verified:
Phase
|
Original binder
|
Test Gap
|
1 mm
|
Test Frequency
|
10.0 rad/s
|
Strain Amplitude
|
12.00 %
|
Stress Amplitude
|
0.196 kPa
|
Phase Angle (δ) (for the 10 cycles)
|
88.8 degree
|
Complex Modulus (G*) (for the 10 measurements)
|
1.634 kPa
|
Test Temperature (Specimen 1)
|
58.0 C
|
Dynamic Shear, G*/sin(δ)
|
1.63 kPa
|