Print Report | Back to Sample Detail

Sample Record for 2022-01-13-10

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 213811 DEA: 112T2184 EFIS: 1116000174 QA Service Level: 1
DIST-CO-RTE-PM: 11-SD-5-R38.4/R47.3
Work Description: (Alternative Delivery) Construct HOV lanes, soundwalls, culvert rehab, ITS, and bike trail on I-5 . NCC I-5 Highway Improvement.
Location Description: IN SAN DIEGO COUNTY IN ENCINITAS AND CARLSBAD FROM SAN ELIJO LAGOON BRIDGE TO 0.3 MILE NORTH OF PALOMAR AIRPORT ROAD OVERCROSSING.
Contractor Name: Flatiron-Skanska-Stacy and Witbeck, a Joint Venture
Contractor Address: 1525 Faraday Ave. #180, Carlsbad, CA 92008
Resident Engineer: Yong Pak Structure Rep.: Cailyn Le

Sample Information

DIME Sample ID: 2022-01-13-10
TL Number from the TL Form:
Sample Submitted By Organization: CT D11 - District 11 Materials Laboratory
Sample Organization Contact: (858) 518-8709
Type of Sample: Quality Assurance
Type of Material: Hot Mix Asphalt
Sample Taken Date: 01/13/2022
Date that the sample was received by the laboratory/organization performing the testing: 01/14/2022
The quantity of what the sample constitutes: 12 Boxes, 3 bags, 2 cans
A brief description of the sample: 1/2" HMA PSU
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Vulcan Otay

Material Information

HMA Type: Type A HMA
HMA Grading: 1/2 inch
Lot number:
Sublot number:
HMA Mix Number:
Binder content (%):
Virgin binder PG:
Design binder PG:
Binder Supplier:
RAP content (%):
WMA Additives:
Antistrip type:
Test results on following page(s): 7

Test Results

Test 1 of 7

DIME Test ID: 2022-01-13-10-1
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 08/29/2024
Date Tested: 01/18/2022
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Pass
Test Result Compliance: complies
Additional Comments When Verified:
What temperature unit is used? Fahrenheit
Test procedure used? Method A
Mass of the specimen basket assembly no data
Mass of the specimen and specimen basket assembly prior to ignition no data
Mass of HMA Sample prior to ignition 1597.6 g
Corrected Asphalt Binder Content 5.57 %
Mass Loss no data
Mass of aggregate remaining after ignition 1501.7 g
Correction Factor (Percent by mass of HMA Specimen) 0.43 %
Moisture Content no data0 %
Temperature Compensation Factor no data
Test Temperature 538 F

Test 2 of 7

DIME Test ID: 2022-01-13-10-2
Test Method: AASHTO T209-12: Standard Method of Test for Theoretical Maximum Specific Gravity (Gmm) and Density of Asphalt Mixtures (Maximum Specific Gravity)
Verified Date: 08/29/2024
Date Tested: 01/20/2022
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Pass
Test Result Compliance: complies
Additional Comments When Verified:
Number of tests 1
What is the unit of measurement for theoretical density? US Units
Mass Determination Water
Specific Gravity for Sample 1 2.518
Theoretical maximum density at 25°C (77°F) no data

Test 3 of 7

DIME Test ID: 2022-01-13-10-3
Test Method: AASHTO T269-14: Standard Method of Test for Percent Air Voids in Compacted Dense and Open Asphalt Mixtures (Air Void)
Verified Date: 08/29/2024
Date Tested: 01/18/2022
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Pass
Test Result Compliance: complies
Additional Comments When Verified:
Percent Air Voids 4.8 %
Percent Air Voids 2 4.9 %
Percent Air Voids 3 5.1 %
Average Percent Air Voids 4.9 %

Test 4 of 7

DIME Test ID: 2022-01-13-10-4
Test Method: AASHTO T275-07r12: Standard Method of Test for Bulk Specific Gravity (Gmb) of Compacted Asphalt Mixtures Using Paraffin-Coated Specimens (Bulk Specific Gravity)
Verified Date: 08/29/2024
Date Tested: 01/18/2022
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: 0519-PSU 2T2184 2022-01-13-10-4
Test Result Compliance: complies
Additional Comments When Verified:
Bulk Specific Gravity 2.397
Bulk Specific Gravity 2 2.394
Bulk Specific Gravity 3 2.389
Average Bulk Specific Gravity 2.393

Test 5 of 7

DIME Test ID: 2022-01-13-10-5
Test Method: AASHTO T283-14: Standard Method of Test for Resistance of Compacted Asphalt Mixtures to Moisture-Induced Damage (Moisture Content)
Verified Date: 08/29/2024
Date Tested: 01/26/2022
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: 0519-PSU 2T2184 2022-01-13-10
Test Result Compliance:
Additional Comments When Verified:
Unit system used? SI Units
Average Dry Tensile Strength 9611 psi
Average Wet Tensile Strength 5878 psi
Tensile Strength Ratio 0.61

Test 6 of 7

DIME Test ID: 2022-01-13-10-7
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 08/29/2024
Date Tested: 01/20/2022
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Oil Content for RAP
Test Result Compliance:
Additional Comments When Verified:
What temperature unit is used? Fahrenheit
Test procedure used? Method A
Mass of the specimen basket assembly no data
Mass of the specimen and specimen basket assembly prior to ignition no data
Mass of HMA Sample prior to ignition 1514.4 g
Corrected Asphalt Binder Content 7.86 %
Mass Loss no data
Mass of aggregate remaining after ignition 1395.4 g
Correction Factor (Percent by mass of HMA Specimen) no data0 %
Moisture Content no data0 %
Temperature Compensation Factor no data
Test Temperature 535.9 F

Test 7 of 7

DIME Test ID: 2022-01-13-10-8
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 08/29/2024
Date Tested: 01/19/2022
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Pass
Test Result Compliance: complies
Additional Comments When Verified:
What temperature unit is used? Fahrenheit
Test procedure used? Method A
Mass of the specimen basket assembly no data
Mass of the specimen and specimen basket assembly prior to ignition no data
Mass of HMA Sample prior to ignition 1558.2 g
Corrected Asphalt Binder Content 5.42 %
Mass Loss no data
Mass of aggregate remaining after ignition 1467.1 g
Correction Factor (Percent by mass of HMA Specimen) 0.43 %
Moisture Content no data0 %
Temperature Compensation Factor no data
Test Temperature 538 F