Print Report | Back to Sample Detail

Sample Record for 2021-07-08-31

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 213411 DEA: 030H10U4 EFIS: 0317000246 QA Service Level: 1
DIST-CO-RTE-PM: 03-SAC-5-9.7/24.9
Work Description:
Location Description: Construction on state highway in Sacramento County in and near Sacramento from 1.1 miles south of Elk Grove Boulevard to American River Viaduct
Contractor Name: NOR CAL PAVING TEICHERT/GRANITE
Contractor Address: 400 Sunrise Ave. Ste. #300, Roseville, CA 95661
Resident Engineer: Daniel Tecle Structure Rep.: Pha Tran

Sample Information

DIME Sample ID: 2021-07-08-31
TL Number from the TL Form: 843944
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 07/08/2021
Date that the sample was received by the laboratory/organization performing the testing: 07/19/2021
The quantity of what the sample constitutes: 1 Can
A brief description of the sample: Asphalt Binder PG 64-16
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Pacific Northwest Oil

Material Information

Performance Grade: PG 64-16
Modified: No
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier: Teichert
Certified Asphalt Supplier: Pacific Northwest Oil - Stockton CA
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:
Test results on following page(s): 6

Test Results

Test 1 of 6

DIME Test ID: 2021-07-08-31-1
Test Method: AASHTO T240-17: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 07/28/2021
Date Tested: 07/21/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified:
Is mass change based on one or two containers? Two
Any material loss from containers during heating process/testing? No
Mass of empty container #1 179.438 grams
Mass of empty container #2 167.932 grams
Mass of container #1 before test (m1i) 215.624 grams
Mass of container #2 before test (m2i) 202.973 grams
Mass of container #1 after test (m1f) 215.452 grams
Mass of container #2 after test (m2f) 202.687 grams
Average mass change -0.646 percent

Test 2 of 6

DIME Test ID: 2021-07-08-31-2
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/28/2021
Date Tested: 07/21/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 Standard Specifications
Test Result Compliance: does not comply
Additional Comments When Verified:
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.100 kPa
Phase Angle (δ) (for the 10 cycles) 87.8 degree
Complex Modulus (G*) (for the 10 measurements) 0.834 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 0.83 kPa

Test 3 of 6

DIME Test ID: 2021-07-08-31-3
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/28/2021
Date Tested: 07/21/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per standard specifications RTFO
Test Result Compliance: complies
Additional Comments When Verified:
Phase RTFO residue
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 10.00 %
Stress Amplitude 0.319 kPa
Phase Angle (δ) (for the 10 cycles) 83.5 degree
Complex Modulus (G*) (for the 10 measurements) 3.185 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 3.21 kPa

Test 4 of 6

DIME Test ID: 2021-07-08-31-4
Test Method: AASHTO T315-20: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/28/2021
Date Tested: 07/22/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per 2018 standard specs PAV
Test Result Compliance: complies
Additional Comments When Verified:
Phase PAV residue
Test Plate Diameter 8 mm
Test Gap 2 mm
Test Frequency 10.0 rad/s
Strain Amplitude 1.00 %
Stress Amplitude 36.510 kPa
Phase Angle (δ) (for the 10 cycles) 48.9 degree
Complex Modulus (G*) (for the 10 measurements) 3650.287 kPa
Test Temperature (Specimen 1) 28.0 C
(G*) x sin(δ)= 2751 kPa

Test 5 of 6

DIME Test ID: 2021-07-08-31-5
Test Method: AASHTO T313-19: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 07/28/2021
Date Tested: 07/25/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: per 2018 standard specifications
Test Result Compliance: complies
Additional Comments When Verified:
Minimum test bath temperature at 240 s -6 C
Maximum test bath temperature at 240 s -6 C
Time of test load application no data HH:MM:SS
File name of test data no data
Time beam in bath no data
Time test started no data HH:MM:SS
Flags issued by software during test no data
Correlation coefficient (R²) no data0
Regression coefficient a no data
Regression coefficient b no data
Regression coefficient c no data
Load at time 0.0 no data0 mN
Deflection at time 0.0 s no data0 µm
Load at time 0.5 s no data0 mN
Deflection at time 0.5 s no data0 µm
Load at 60.0 s 998 mN
Beam deflection 60.0 s 1.187 µm
Measured Stiffness Modulus 60.0 s 67.8 mPa
Estimated Stiffness Modulus 60.0 s 67.8 mPa
Difference between stiffness moduli 60.0 s no data
Estimated m-value 60.0 s 0.402

Test 6 of 6

DIME Test ID: 2021-07-08-31-6
Test Method: AASHTO T315-16: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/28/2021
Date Tested: 07/21/2021
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard, Room 225,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (916) 227-7302
General Comments for this Test: Per standard specifications ORIG 2
Test Result Compliance: does not comply
Additional Comments When Verified: Failed T315 Original
Phase Original binder
Test Plate Diameter 25 mm
Test Gap 1 mm
Test Frequency 10.0 rad/s
Strain Amplitude 12.00 %
Stress Amplitude 0.102 kPa
Phase Angle (δ) (for the 10 cycles) 87.8 degree
Complex Modulus (G*) (for the 10 measurements) 0.854 kPa
Test Temperature (Specimen 1) 64.0 C
Dynamic Shear, G*/sin(δ) 0.85 kPa