Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
DEA: No Project
QA Service Level:
DIST-CO-RTE-PM: ---
Work Description: Special project identifier for material not associated with a project
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2018-08-30-5
TL Number from the TL Form: NA
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (530) 329-6527
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Ductile Iron Cast Samples
Sample Taken Date: 08/30/2018
Date that the sample was received by the laboratory/organization performing the testing: 08/31/2018
The quantity of what the sample constitutes: 15
A brief description of the sample: Ductile Iron Casting
From where was the sample collected: Distributor
Laboratory sample identification: Unknown
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: SDI Farrar
Heat Number (s): E168 E178 D188 D198 D258 E038 E098 F018 F068
Part Number (s): 1 75 HS 1 38 HS 1 75 HS 1 75 HS 1 75 HS 19 6
Material Specification: A536
Grades: 80-55-06
Metal Foundry Manufacturer (Mill): Farrar Corporation
Prestressing Manufacturer: SDI
DIME Test ID: 2018-08-30-5-1
Test Method: ASTM A370-15: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 09/10/2018
Date Tested: 09/06/2018
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: joshua.moore@dot.ca.gov
Organization Phone: (530) 329-6527
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
|
Number of Samples
|
15
|
| Sample | Heat Number | Diameter (in) | Area (sqin) | Stress at Offset (psi) | Tensile Strength (psi) | Elongation in 4 x d (%) | Tested By | | E098 | 0.501 | 0.1971 | 65833 | 112930 | 7.2 | Fred | | F018 | 0.501 | 0.1971 | 59983 | 103560 | 10.3 | Fred | | D198 | 0.501 | 0.1971 | 62339 | 109070 | 8.2 | Fred | | D258 | 0.501 | 0.1971 | 64766 | 113580 | 8 | Fred | | E168 | 0.501 | 0.1971 | 64992 | 113270 | 6.9 | Fred | | F068 | 0.501 | 0.1971 | 63910 | 111590 | 9.4 | Fred | | F068A | 0.501 | 0.1971 | 64690 | 109900 | 8 | Fred | | F078 | 0.502 | 0.1979 | 62866 | 110700 | 9.2 | Fred | | D188 | 0.501 | 0.1971 | 64246 | 112930 | 10.1 | Fred | | F278 | 0.501 | 0.1971 | 65267 | 113610 | 7.1 | Fred | | F298 | 0.501 | 0.1971 | 64717 | 113680 | 8.3 | Fred | | E178 | 0.501 | 0.1971 | 65351 | 115160 | 7.5 | Fred | | F138 | 0.501 | 0.1971 | 63272 | 111000 | 9.4 | Fred | | E038 | 0.501 | 0.1971 | 65361 | 114030 | 10.7 | Fred | | F148 | 0.501 | 0.1971 | 64637 | 114230 | 9.2 | Fred |
| |
|
UTM
|
67KIP
|
|
Temperature
|
72 F
|