Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 1001213 DEA: 11431644 EFIS: 1122000232
QA Service Level: 1
DIST-CO-RTE-PM: 11-SD-78-N17.7
Work Description: Cold plane, RHMA overlay, Concrete Barriers, Landscape and Electrical.
Location Description: IN SAN DIEGO COUNTY FROM ROUTE 78/5 SEPARATION TO 0.3 MILE EAST OF ESCONDIDO BOULEVARD UNDERCROSSING.
Contractor Name: Skanska USA Civil West
Contractor Address: 1995 Agua Mansa Rd., Riverside, CA 92509
Resident Engineer: Yong Pak Structure Rep.: Carlos Lopez
DIME Sample ID: 2026-08-06-115
TL Number from the TL Form:
Sample Submitted By Organization: CT D11 - District 11 Materials Laboratory
Sample Organization Contact: (858) 518-8709
Type of Sample: Quality Assurance
Type of Material: Hot Mix Asphalt
Sample Taken Date: 08/06/2026
Date that the sample was received by the laboratory/organization performing the testing: 08/07/2026
The quantity of what the sample constitutes: 4 boxes
A brief description of the sample: 1/2" RHMA-G
From where was the sample collected: Supplier
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: RJ Noble Corona
DIME Test ID: 2026-08-06-115-1
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 10/02/2026
Date Tested: 10/01/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: COMPLIES
Test Result Compliance: complies
Additional Comments When Verified:
|
What temperature unit is used?
|
Celsius
|
|
Test procedure used?
|
Method A
|
|
Mass of the specimen basket assembly
|
3926 g
|
|
Mass of the specimen and specimen basket assembly prior to ignition
|
5473.6 g
|
|
Mass of HMA Sample prior to ignition
|
1547.6 g
|
|
Corrected Asphalt Binder Content
|
7.42 %
|
|
Mass Loss
|
119.9 g
|
|
Mass of aggregate remaining after ignition
|
1427.7 g
|
|
Correction Factor (Percent by mass of HMA Specimen)
|
0.33 %
|
|
Moisture Content
|
no data0 %
|
|
Temperature Compensation Factor
|
no data0 %
|
|
Test Temperature
|
538 C
|
DIME Test ID: 2026-08-06-115-2
Test Method: AASHTO T209-25: Standard Method of Test for Theoretical Maximum Specific Gravity (Gmm) and Density of Asphalt Mixtures (Maximum Specific Gravity)
Verified Date: 10/02/2026
Date Tested: 10/02/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test:
Test Result Compliance: not applicable
Additional Comments When Verified:
|
Number of Samples
|
1
|
|
What is the unit of measurement for theoretical density?
|
SI Units
|
|
Mass Determination
|
Air
|
|
Method Performed
|
Mechanical Agitation - Method A
|
|
Mass of container filled with water 1
|
7475.6 grams
|
|
Mass of oven-dry sample in air for Sample 1
|
1559.8 grams
|
|
Mass of container filled with the sample and water for Sample 1
|
8393.7 grams
|
|
Temperature of Water
|
77 °F
|
|
Specific Gravity for Sample 1
|
2.431
|
|
Theoretical maximum density at 25°C (77°F)
|
2424 kg/m^3
|
DIME Test ID: 2026-08-06-115-3
Test Method: CTM 375-February 2012: Determining the Density and Relative Compaction of Data Cores (lab)
Verified Date: 10/02/2026
Date Tested: 10/02/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: COMPLIES
Test Result Compliance: complies
Additional Comments When Verified:
|
Number of Cores
|
5
|
|
Core 5 ID
|
7B34
|
|
Dry Weight 5
|
805.9 grams
|
|
Parrafin Coated Weight 5
|
821.9 grams
|
|
Coated Weight in Water 5
|
441.7 grams
|
|
Core ID
|
7A33
|
|
Dry Weight
|
782.3 grams
|
|
Parrafin Coated Weight
|
797.8 grams
|
|
Coated Weight in Water
|
429.1 grams
|
|
Theoretical Maximum Density
|
2.431
|
|
Core 2 ID
|
7B33
|
|
Dry Weight 2
|
757.4 grams
|
|
Parrafin Coated Weight 2
|
773.6 grams
|
|
Coated Weight in Water 2
|
414.4 grams
|
|
Core 3 ID
|
7C33
|
|
Dry Weight 3
|
785 grams
|
|
Parrafin Coated Weight 3
|
798.5 grams
|
|
Coated Weight in Water 3
|
435.1 grams
|
|
Core 4 ID
|
7A34
|
|
Dry Weight 4
|
724.8 grams
|
|
Parrafin Coated Weight 4
|
737.1 grams
|
|
Coated Weight in Water 4
|
403.2 grams
|