Sample Information

DIME Sample ID: 2026-06-30-38
TL Number from the TL Form:
Sample Submitted By Organization: CT D11 - District 11 Materials Laboratory
Sample Organization Contact: (858) 518-8709
Type of Sample: Quality Assurance
Type of Material: Hot Mix Asphalt
Sample Taken Date: 06/30/2026
Date that the sample was received by the laboratory/organization performing the testing: 06/30/2026
The quantity of what the sample constitutes: 4 boxes
A brief description of the sample: Plant Sample
From where was the sample collected: Supplier
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Vulcan Otay

Material Information

HMA Type: RHMA-G
HMA Grading: 3/4 inch
Lot number:
Sublot number:
HMA Mix Number: 226110
Binder content (%): 7.5
Virgin binder PG:
Design binder PG:
Binder Supplier:
RAP content (%): 0
WMA Additives:
Antistrip type:
Test results on following page(s): 4

Test Results

Test

DIME Test ID: 2026-06-30-38-1
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 07/23/2026
Date Tested: 07/17/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Target (7.5-0.5)%= 7.00%, 6.50%<7.00%,does not comply
Test Result Compliance: does not comply
Additional Comments When Verified:
What temperature unit is used? Celsius
Test procedure used? Method A
Mass of the specimen basket assembly 4045.1 g
Mass of the specimen and specimen basket assembly prior to ignition 6088.6 g
Mass of HMA Sample prior to ignition 2043.5 g
Corrected Asphalt Binder Content 6.5 %
Mass Loss 148.2 g
Mass of aggregate remaining after ignition 1895.3 g
Correction Factor (Percent by mass of HMA Specimen) 0.75 %
Moisture Content no data0 %
Temperature Compensation Factor no data0 %
Test Temperature 538 C

Test

DIME Test ID: 2026-06-30-38-2
Test Method: AASHTO T209-12: Standard Method of Test for Theoretical Maximum Specific Gravity (Gmm) and Density of Asphalt Mixtures (Maximum Specific Gravity)
Verified Date: 07/14/2026
Date Tested: 07/17/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: complies
Test Result Compliance: complies
Additional Comments When Verified:
Number of tests 1
What is the unit of measurement for theoretical density? SI Units
Mass Determination Air
Method Performed Mechanical Agitation - Method A
Mass of container filled with water 7475.6 grams
Mass of oven-dry sample in air for Sample 1 2556.4 grams
Mass of container filled with the sample and water for Sample 1 8975.8 grams
Temperature of Water 77 °F
Specific Gravity for Sample 1 2.42
Theoretical maximum density at 25°C (77°F) 2413 kg/m^3

Test

DIME Test ID: 2026-06-30-38-3
Test Method: CTM 375-February 2012: Determining the Density and Relative Compaction of Data Cores (lab)
Verified Date: 07/14/2026
Date Tested: 07/10/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Complies
Test Result Compliance: complies
Additional Comments When Verified:
Number of Cores 2
Core ID 1-QA
Dry Weight 704.3 grams
Parrafin Coated Weight 715.7 grams
Coated Weight in Water 389.7 grams
Theoretical Maximum Density 2.42
Core 2 ID 2QA
Dry Weight 2 808.5 grams
Parrafin Coated Weight 2 823.1 grams
Coated Weight in Water 2 444.8 grams

Test

DIME Test ID: 2026-06-30-38-4
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 08/14/2026
Date Tested: 08/14/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Retest Oven 1, does not comply, tested 6.88%, target 7.1% min.
Test Result Compliance: does not comply
Additional Comments When Verified:
What temperature unit is used? Celsius
Test procedure used? Method A
Mass of the specimen basket assembly 3923.5 g
Mass of the specimen and specimen basket assembly prior to ignition 5958.9 g
Mass of HMA Sample prior to ignition 2035.4 g
Corrected Asphalt Binder Content 6.88 %
Mass Loss 155.2 g
Mass of aggregate remaining after ignition 1880.2 g
Correction Factor (Percent by mass of HMA Specimen) 0.75 %
Moisture Content no data0 %
Temperature Compensation Factor no data0 %
Test Temperature 538 C