Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 1001213 DEA: 11431644 EFIS: 1122000232
QA Service Level: 1
DIST-CO-RTE-PM: 11-SD-78-N17.7
Work Description: Cold plane, RHMA overlay, Concrete Barriers, Landscape and Electrical.
Location Description: IN SAN DIEGO COUNTY FROM ROUTE 78/5 SEPARATION TO 0.3 MILE EAST OF ESCONDIDO BOULEVARD UNDERCROSSING.
Contractor Name: Skanska USA Civil West
Contractor Address: 1995 Agua Mansa Rd., Riverside, CA 92509
Resident Engineer: Yong Pak Structure Rep.: Carlos Lopez
DIME Sample ID: 2026-05-20-11
TL Number from the TL Form:
Sample Submitted By Organization: CT D11 - District 11 Materials Laboratory
Sample Organization Contact: (858) 518-8709
Type of Sample: Quality Assurance
Type of Material: Hot Mix Asphalt
Sample Taken Date: 05/20/2026
Date that the sample was received by the laboratory/organization performing the testing: 05/20/2026
The quantity of what the sample constitutes: 4 boxes
A brief description of the sample: JMFR
From where was the sample collected: Supplier
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: RJ Noble Corona
DIME Test ID: 2026-05-20-11-1
Test Method: CTM 375-February 2012: Determining the Density and Relative Compaction of Data Cores (lab)
Verified Date: 06/01/2026
Date Tested: 06/01/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Complies
Test Result Compliance: complies
Additional Comments When Verified:
|
Number of Cores
|
3
|
|
Core ID
|
6A30
|
|
Dry Weight
|
954.8 grams
|
|
Parrafin Coated Weight
|
973.6 grams
|
|
Coated Weight in Water
|
524.8 grams
|
|
Theoretical Maximum Density
|
2.43
|
|
Core 2 ID
|
6B30
|
|
Dry Weight 2
|
1099.4 grams
|
|
Parrafin Coated Weight 2
|
1115 grams
|
|
Coated Weight in Water 2
|
617.4 grams
|
|
Core 3 ID
|
6C30
|
|
Dry Weight 3
|
1239.4 grams
|
|
Parrafin Coated Weight 3
|
1259.6 grams
|
|
Coated Weight in Water 3
|
681 grams
|
DIME Test ID: 2026-05-20-11-2
Test Method: CTM 375-February 2012: Determining the Density and Relative Compaction of Data Cores (lab)
Verified Date: 06/01/2026
Date Tested: 06/01/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Complies
Test Result Compliance: complies
Additional Comments When Verified:
|
Number of Cores
|
1
|
|
Core ID
|
6A31
|
|
Dry Weight
|
1032.8 grams
|
|
Parrafin Coated Weight
|
1048.7 grams
|
|
Coated Weight in Water
|
574.4 grams
|
|
Theoretical Maximum Density
|
2.43
|
DIME Test ID: 2026-05-20-11-3
Test Method: AASHTO T209-12: Standard Method of Test for Theoretical Maximum Specific Gravity (Gmm) and Density of Asphalt Mixtures (Maximum Specific Gravity)
Verified Date: 06/01/2026
Date Tested: 05/29/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: N/A
Test Result Compliance: not applicable
Additional Comments When Verified:
|
Number of tests
|
1
|
|
What is the unit of measurement for theoretical density?
|
SI Units
|
|
Mass Determination
|
Air
|
|
Method Performed
|
Mechanical Agitation - Method A
|
|
Mass of container filled with water
|
7149.5 grams
|
|
Mass of oven-dry sample in air for Sample 1
|
2517.8 grams
|
|
Mass of container filled with the sample and water for Sample 1
|
8631.2 grams
|
|
Temperature of Water
|
77 °F
|
|
Specific Gravity for Sample 1
|
2.43
|
|
Theoretical maximum density at 25°C (77°F)
|
2423 kg/m^3
|
DIME Test ID: 2026-05-20-11-4
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 06/01/2026
Date Tested: 05/29/2026
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Target 7.5% tested 7.67%,
complies, Oven# 1
Test Result Compliance: complies
Additional Comments When Verified:
|
What temperature unit is used?
|
Celsius
|
|
Test procedure used?
|
Method A
|
|
Mass of the specimen basket assembly
|
4033.7 g
|
|
Mass of the specimen and specimen basket assembly prior to ignition
|
6098.8 g
|
|
Mass of HMA Sample prior to ignition
|
2065.1 g
|
|
Corrected Asphalt Binder Content
|
7.67 %
|
|
Mass Loss
|
168.2 g
|
|
Mass of aggregate remaining after ignition
|
1896.9 g
|
|
Correction Factor (Percent by mass of HMA Specimen)
|
0.47 %
|
|
Moisture Content
|
no data0 %
|
|
Temperature Compensation Factor
|
no data0 %
|
|
Test Temperature
|
538 C
|