Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 88888 DEA: SMTL-STOCK EFIS: SMTL-STOCK
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2026-02-16-4
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (213) 505-4213
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Ductile Iron Cast Samples
Sample Taken Date: 02/16/2026
Date that the sample was received by the laboratory/organization performing the testing: 03/12/2026
The quantity of what the sample constitutes: 2301
A brief description of the sample: Iron Ductile Castings
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Schwagger Davis
Heat Number (s): B116, A226, B056, B036, A226, L035, K195
Part Number (s): SDI 31 6 AH SDI 27 PC BP SD I12 6 AH SDI 19
Material Specification: A536
Grades: 80-55-06
Metal Foundry Manufacturer (Mill): Farrar Corporation
Prestressing Manufacturer: Schwager Davis Inc
DIME Test ID: 2026-02-16-4-1
Test Method: ASTM A370-20: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 04/07/2026
Date Tested: 04/07/2026
Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: brian.ellis@dot.ca.gov
Organization Phone: (916) 380-8623
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
|
Number of Samples
|
7
|
| Sample | Heat Number | Diameter (in) | Area (sqin) | Stress at Offset (psi) | Tensile Strength (psi) | Elongation in 4 x d (%) | Tested By | | 1 | A226 19 6pc1 | 0.506 | 0.2011 | 66100 | 109100 | 7 | Atlas | | 2 | A226 31 6s | 0.506 | 0.2011 | 66600 | 106500 | 8 | Atlas | | 3 | B036 | 0.506 | 0.2011 | 65200 | 111600 | 9 | Atlas | | 4 | B056 | 0.506 | 0.2011 | 65400 | 107800 | 8 | Atlas | | 5 | B116 | 0.506 | 0.2011 | 65900 | 103900 | 8 | Atlas | | 6 | L035 | 0.506 | 0.2011 | 62800 | 101000 | 8 | Atlas | | 7 | K195 | 0.507 | 0.2019 | 66600 | 105900 | 7 | Atlas |
| |
|
UTM
|
NA
|
|
Temperature
|
0 f
|