Print Report | Back to Sample Detail

Sample Record for 2025-08-27-61

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 1000017 DEA: 042Q7004 EFIS: 0419000040 QA Service Level: 1
DIST-CO-RTE-PM: 04-CC-4-L0.0/R14.3
Work Description: REPLACE ASPHALT CONCRETE SURFACING AND INSTALL MGS.
Location Description: CONTRA COSTA COUNTY IN HERCULES AND CONCORD FROM SAN PABLO AVENUE TO ROUTE 4/242 SEPARATION
Contractor Name: BAY CITIES PAVING & GRADING, INC.
Contractor Address: Unknown
Resident Engineer: Rabindra Mukherjee Structure Rep.: John K. Parecadan

Sample Information

DIME Sample ID: 2025-08-27-61
TL Number from the TL Form: Sacramento Caltrans lab
Sample Submitted By Organization: Kwik Bond Polymers
Sample Organization Contact: (760) 518-6064
Type of Sample: Quality Control
Type of Material: High Friction Surface Treatment
Sample Taken Date: 08/27/2025
Date that the sample was received by the laboratory/organization performing the testing: 08/28/2025
The quantity of what the sample constitutes: 21 Totes
A brief description of the sample: 1 gallon can HFST Resin
From where was the sample collected: Source
Laboratory sample identification: 000178KBP
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Kwik Bond Polymers, Benicia

Material Information

Mgf. Lot Number(s): AZ5H01066
Batch Number: AZ5H01066
Mix Number: AZ5H01066
Resin Binder Type: Polyester
Used for Overlay: Yes
Used for Inlay: No
Test results on following page(s): 2

Test Results

Test 1 of 2

DIME Test ID: 2025-08-27-61-1
Test Method: ASTM D2196-Feb15: Standard Test Methods for Rheological Properties of Non-Newtonian Materials by Rotational Viscometer
Verified Date: 10/15/2025
Date Tested: 10/10/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test: Gel Time (ASTM C881): 31 mins. (Does not comply) Cure Rate (ASTM D1640): 95 mins. (Complies)
Test Result Compliance: complies
Additional Comments When Verified:
Viscosity 1664

Test 2 of 2

DIME Test ID: 2025-08-27-61-2
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Verified Date: 10/15/2025
Date Tested: 10/10/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Number of specimens tested 5
Conditioning procedure 18/25/50+5/70
Speed of testing 0.45 in/min
Sample 1 Width 0.483 in
Sample 1 Ultimate strength 3157.1 psi
Sample 1 Thickness 0.137 in
Sample 1 Area 0.0662 in^2
Sample 1 Ultimate Strength Actual 209 lbs
Sample 1 percent elongation 49 %
Sample 1 Time no data0 MM:SS
Sample 2 Width 0.486 in
Sample 2 Thickness 0.127 in
Sample 2 Area 0.0617 in^2
Sample 2 Ultimate strength 3419.8 psi
Sample 2 Ultimate Strength Actual 211 lbs
Sample 2 percent elongation 63 %
Sample 2 Time no data0 MM:SS
Sample 3 Width 0.488 in
Sample 3 Thickness 0.133 in
Sample 3 Area 0.0649 in^2
Sample 3 Ultimate strength 3020 psi
Sample 3 Ultimate Strength Actual 196 lbs
Sample 3 percent elongation 43 %
Sample 3 Time no data0 MM:SS
Sample 4 Width 0.486 in
Sample 4 Thickness 0.137 in
Sample 4 Area 0.0666 in^2
Sample 4 Ultimate strength 3933.9 psi
Sample 4 Ultimate Strength Actual 262 lbs
Sample 4 percent elongation 71 %
Sample 4 Time no data0 MM:SS
Sample 5 Width 0.483 in
Sample 5 Thickness 0.131 in
Sample 5 Area 0.0633 in^2
Sample 5 Ultimate strength 3712.5 psi
Sample 5 Ultimate Strength Actual 235 lbs
Sample 5 percent elongation 72 %
Sample 5 Time no data0 MM:SS
Ultimate Strength Average 3449 psi
Percent Elongation Average 60 %