Print Report | Back to Sample Detail

Sample Record for 2025-08-10-18

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 1000211 DEA: 112N0204 EFIS: 1117000168 QA Service Level: 1
DIST-CO-RTE-PM: 11-SD-76-R17.2/24.1
Work Description: COLD PLANE AND OVERLAY WITH RHMA GAP GRADED.
Location Description: SAN DIEGO COUNTY NEAR PALA FROM ROUTE 76/15 SEPARATION TO PALA MISSION ROAD
Contractor Name: GRIFFITH COMPANY
Contractor Address: 13400 Sabre Spring Parkway Ste 200, San Diego, CA 92128
Resident Engineer: Fahad Masud Structure Rep.: Unknown

Sample Information

DIME Sample ID: 2025-08-10-18
TL Number from the TL Form:
Sample Submitted By Organization: CT D11 - District 11 Materials Laboratory
Sample Organization Contact: (858) 518-8709
Type of Sample: Per Request
Type of Material: Hot Mix Asphalt
Sample Taken Date: 08/10/2025
Date that the sample was received by the laboratory/organization performing the testing: 08/11/2025
The quantity of what the sample constitutes: 4 Boxes
A brief description of the sample: Plant Sample
From where was the sample collected: Supplier
Laboratory sample identification: 25-08-10-18-A
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Vulcan Corona

Material Information

HMA Type: RHMA-G
HMA Grading: 1/2 inch
Lot number:
Sublot number:
HMA Mix Number: 326122 CORD SJR
Binder content (%): 7.5
Virgin binder PG: PG 64-16
Design binder PG: PG 64-16
Binder Supplier: SJR
RAP content (%): 0
WMA Additives: Yes
Antistrip type:
Test results on following page(s): 3

Test Results

Test 1 of 3

DIME Test ID: 2025-08-10-18-1
Test Method: AASHTO T308-10: Standard Method of Test for Determining the Asphalt Binder Content of Hot Mix Asphalt (HMA) by the Ignition Method (Method A) (Asphalt Binder Content)
Verified Date: 09/09/2025
Date Tested: 09/02/2025
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Target 7.5%
Test Result Compliance: complies
Additional Comments When Verified:
What temperature unit is used? Fahrenheit
Test procedure used? Method A
Mass of the specimen basket assembly 3932.9 g
Mass of the specimen and specimen basket assembly prior to ignition 5487.1 g
Mass of HMA Sample prior to ignition 1554.2 g
Corrected Asphalt Binder Content 7.26 %
Mass Loss 117.4 g
Mass of aggregate remaining after ignition 1436.8 g
Correction Factor (Percent by mass of HMA Specimen) 0.29 %
Moisture Content no data0 %
Temperature Compensation Factor no data0 %
Test Temperature 538 F

Test 2 of 3

DIME Test ID: 2025-08-10-18-2
Test Method: AASHTO T209-12: Standard Method of Test for Theoretical Maximum Specific Gravity (Gmm) and Density of Asphalt Mixtures (Maximum Specific Gravity)
Verified Date: 09/09/2025
Date Tested: 09/03/2025
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test: Target 2.436 / Tested 2.459
Test Result Compliance: complies
Additional Comments When Verified:
Number of tests 1
What is the unit of measurement for theoretical density? US Units
Mass Determination Air
Method Performed no data
Mass of container filled with water 7475.6 grams
Mass of oven-dry sample in air for Sample 1 1528.8 grams
Mass of container filled with the sample and water for Sample 1 8382.8 grams
Temperature of Water 77 °F
Specific Gravity for Sample 1 2.459
Theoretical maximum density at 25°C (77°F) 153.1 lb/ft^3

Test 3 of 3

DIME Test ID: 2025-08-10-18-3
Test Method: CTM 375-February 2012: Determining the Density and Relative Compaction of Data Cores (lab)
Verified Date: 12/09/2025
Date Tested: 12/03/2025
Submitted By Organization: CT D11 - District 11 Materials Laboratory
Organization Address: 4050 Taylor Street,
Organization City: San Diego
Organization State: CA
Organization Zipcode: 92110
Organization Email: benjamin.haney@dot.ca.gov
Organization Phone: (858) 688-1595
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Number of Cores 4
Core 1 ID 3 A
Dry Weight 1 823.8 grams
Parrafin Coated Weight 1 849.7 grams
Coated Weight in Water 1 456.9 grams
Theoretical Maximum Density 2.459
Core 2 ID 3 A
Dry Weight 2 1025.9 grams
Parrafin Coated Weight 2 1044.2 grams
Coated Weight in Water 2 568.6 grams
Core 3 ID 3 C
Dry Weight 3 978.6 grams
Parrafin Coated Weight 3 999.2 grams
Coated Weight in Water 3 531.5 grams
Core 4 ID 4 A
Dry Weight 4 989.2 grams
Parrafin Coated Weight 4 1006.1 grams
Coated Weight in Water 4 545.4 grams
Sublot Relative Compaction 91 %