Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 44444 DEA: ASCP EFIS: ASCP
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for submitting Sample information for Asphalt Supplier Certification Program.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2025-05-23-37
TL Number from the TL Form:
Sample Submitted By Organization: Atlas - Denver
Sample Organization Contact: 303-975-9959
Type of Sample: Verification
Type of Material: Asphalt Binder
Sample Taken Date: 05/23/2025
Date that the sample was received by the laboratory/organization performing the testing: 06/23/2025
The quantity of what the sample constitutes: 1 of 2
A brief description of the sample: Tank 08
From where was the sample collected: Manufacturer
Laboratory sample identification: TK0805232025
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Mojave, CA
Performance Grade: PG 58-22
Modified:
Lot number:
Sublot number:
Tank number:
Time of sample: 10:00
HMA Supplier:
Certified Asphalt Supplier: Pacific Asphalt Distribution - Mojave CA
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:
DIME Test ID: 2025-05-23-37-1
Test Method: AASHTO T315-24: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/11/2025
Date Tested: 07/08/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: Original
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
Original binder
|
|
Test Gap
|
1 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
12.06 %
|
|
Stress Amplitude
|
0.173 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
88.1 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
1.438 kPa
|
|
Test Temperature (Specimen 1)
|
58.0 C
|
|
Dynamic Shear, G*/sin(δ)
|
1.44 kPa
|
DIME Test ID: 2025-05-23-37-2
Test Method: AASHTO T315-24: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/11/2025
Date Tested: 07/11/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: RTFO
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
RTFO residue
|
|
Test Gap
|
1 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
10.05 %
|
|
Stress Amplitude
|
0.336 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
85.5 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
3.338 kPa
|
|
Test Temperature (Specimen 1)
|
58.0 C
|
|
Dynamic Shear, G*/sin(δ)
|
3.35 kPa
|
DIME Test ID: 2025-05-23-37-3
Test Method: AASHTO T315-24: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 07/11/2025
Date Tested: 07/09/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: PAV
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
PAV residue
|
|
Test Plate Diameter
|
8 mm
|
|
Test Gap
|
2 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
1.01 %
|
|
Stress Amplitude
|
58.550 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
51.2 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
5825.615 kPa
|
|
Test Temperature (Specimen 1)
|
22.0 C
|
|
(G*) x sin(δ)=
|
4540 kPa
|
DIME Test ID: 2025-05-23-37-4
Test Method: AASHTO T51-22: Standard Method of Test for Ductility of Asphalt Materials (Asphalt Binder)
Verified Date: 07/11/2025
Date Tested: 07/09/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: Ductility
Test Result Compliance: complies
Additional Comments When Verified:
|
Is a normal test obtainable?
|
Yes
|
|
Number of replicates tested
|
Three
|
|
Ductility of test #1 (D1)
|
150 cm
|
|
Ductility of test #2 (D2)
|
150 cm
|
|
Ductility of test #3 (D3)
|
150 cm
|
|
Ductility of sample
|
150 cm
|
DIME Test ID: 2025-05-23-37-5
Test Method: AASHTO T240-23: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 07/11/2025
Date Tested: 07/09/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: Mass Change
Test Result Compliance: complies
Additional Comments When Verified:
|
Is mass change based on one or two containers?
|
Two
|
|
Is mass change correction factor needed?
|
Yes
|
|
Any material loss from containers during heating process/testing?
|
No
|
|
Mass of container #1 before test (m1i)
|
211.229 grams
|
|
Mass of container #2 before test (m2i)
|
207.692 grams
|
|
Mass of container #1 after test (m1f)
|
211.2 grams
|
|
Mass of container #2 after test (m2f)
|
207.646 grams
|
|
Average mass change
|
-0.078 percent
|
|
Mass of empty container #1
|
176.08 grams
|
|
Mass of empty container #2
|
173.034 grams
|
|
Mass correction factor
|
0.03
|
DIME Test ID: 2025-05-23-37-7
Test Method: AASHTO T313-22: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 07/11/2025
Date Tested: 07/09/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: BBR
Test Result Compliance: complies
Additional Comments When Verified:
|
Minimum test bath temperature at 240 s
|
-12 C
|
|
Maximum test bath temperature at 240 s
|
-11.9 C
|
|
Time of test load application
|
no data HH:MM:SS
|
|
File name of test data
|
no data
|
|
Time beam in bath
|
no data
|
|
Time test started
|
no data HH:MM:SS
|
|
Flags issued by software during test
|
no data
|
|
Correlation coefficient (R²)
|
no data0
|
|
Regression coefficient a
|
no data
|
|
Regression coefficient b
|
no data
|
|
Regression coefficient c
|
no data
|
|
Load at time 0.0
|
no data0 mN
|
|
Deflection at time 0.0 s
|
no data0 µm
|
|
Load at time 0.5 s
|
no data0 mN
|
|
Deflection at time 0.5 s
|
no data0 µm
|
|
Load at 60.0 s
|
no data0 mN
|
|
Beam deflection 60.0 s
|
no data0 µm
|
|
Measured Stiffness Modulus 60.0 s
|
no data
|
|
Estimated Stiffness Modulus 60.0 s
|
182.5 MPa
|
|
Difference between stiffness moduli 60.0 s
|
no data
|
|
Estimated m-value 60.0 s
|
0.35
|
DIME Test ID: 2025-05-23-37-8
Test Method: AASHTO T316-22: Standard Method of Test for Viscosity Determination of Asphalt Binder Using Rotational Viscometer
Verified Date: 07/11/2025
Date Tested: 07/08/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: Viscosity @135C
Test Result Compliance: complies
Additional Comments When Verified:
|
Is viscosity reading in cP/Pa-s?
|
cP
|
|
Time of test
|
00:00 HH:MM
|
|
Test Temperature
|
135 C
|
|
Speed
|
20 rpm
|
|
Spindle size
|
.463 in
|
|
Torque
|
10 %
|
|
Viscosity reading #1 (A)
|
249.9 cP
|
|
Viscosity reading #2 (B)
|
250 cP
|
|
Viscosity reading #3 (C)
|
250 cP
|
|
Average viscosity
|
0.25 Pa-s
|