Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 1000698 DEA: 024H0704 EFIS: 0218000074
QA Service Level: 1
DIST-CO-RTE-PM: 02-LAS-139-0.74/11.0
Work Description: PLACE HMA (TYPE A), TRAFFIC CONTROL SYSTEM, TRAFFIC STRIPE, RDWY EXC.
Location Description: LASSEN COUNTY NEAR SUSANVILLE FROM 0.1 MILE NORTH OF CHESTNUT STREET TO 2.6 MILES SOUTH OF HORSE LAKE ROAD
Contractor Name: HAT CREEK CONSTRUCTION & MATERIALS, INC.
Contractor Address: Unknown
Resident Engineer: Daniel Gibbs Structure Rep.: Tooraj Yegan
DIME Sample ID: 2025-05-22-51
TL Number from the TL Form: 867337
Sample Submitted By Organization: Atlas - Denver
Sample Organization Contact: 303-975-9959
Type of Sample: Quality Assurance
Type of Material: Asphalt Binder
Sample Taken Date: 05/22/2025
Date that the sample was received by the laboratory/organization performing the testing: 06/02/2025
The quantity of what the sample constitutes: 2 Cans
A brief description of the sample: PG 58-34
From where was the sample collected: Job Site
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Hot Creek Word Lake
Performance Grade: PG 58-34
Modified: No
Lot number:
Sublot number:
Tank number:
Time of sample:
HMA Supplier:
Certified Asphalt Supplier: Albina Asphalt (Klamath Falls Plant) - Klamath Falls OR
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:
DIME Test ID: 2025-05-22-51-1
Test Method: AASHTO T315-24: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 06/25/2025
Date Tested: 06/11/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: Original
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
Original binder
|
|
Test Gap
|
1 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
12.06 %
|
|
Stress Amplitude
|
0.151 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
82.1 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
1.253 kPa
|
|
Test Temperature (Specimen 1)
|
58.0 C
|
|
Dynamic Shear, G*/sin(δ)
|
1.27 kPa
|
DIME Test ID: 2025-05-22-51-2
Test Method: AASHTO T315-24: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 06/25/2025
Date Tested: 06/24/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: RTFO
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
RTFO residue
|
|
Test Gap
|
1 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
10.05 %
|
|
Stress Amplitude
|
0.927 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
64.7 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
9.227 kPa
|
|
Test Temperature (Specimen 1)
|
58.0 C
|
|
Dynamic Shear, G*/sin(δ)
|
10.21 kPa
|
DIME Test ID: 2025-05-22-51-3
Test Method: AASHTO T315-24: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 06/25/2025
Date Tested: 06/12/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: PAV
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
PAV residue
|
|
Test Plate Diameter
|
8 mm
|
|
Test Gap
|
2 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
1.01 %
|
|
Stress Amplitude
|
50.656 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
39.3 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
5040.184 kPa
|
|
Test Temperature (Specimen 1)
|
16.0 C
|
|
(G*) x sin(δ)=
|
3192 kPa
|
DIME Test ID: 2025-05-22-51-4
Test Method: AASHTO T313-22: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 06/25/2025
Date Tested: 06/12/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: BBR
Test Result Compliance: complies
Additional Comments When Verified:
|
Minimum test bath temperature at 240 s
|
-24 C
|
|
Maximum test bath temperature at 240 s
|
-24 C
|
|
Time of test load application
|
01:51:35 HH:MM:SS
|
|
File name of test data
|
no data
|
|
Time beam in bath
|
no data
|
|
Time test started
|
no data HH:MM:SS
|
|
Flags issued by software during test
|
no data
|
|
Correlation coefficient (R²)
|
no data0
|
|
Regression coefficient a
|
no data
|
|
Regression coefficient b
|
no data
|
|
Regression coefficient c
|
no data
|
|
Load at time 0.0
|
no data0 mN
|
|
Deflection at time 0.0 s
|
no data0 µm
|
|
Load at time 0.5 s
|
no data0 mN
|
|
Deflection at time 0.5 s
|
no data0 µm
|
|
Load at 60.0 s
|
no data0 mN
|
|
Beam deflection 60.0 s
|
no data0 µm
|
|
Measured Stiffness Modulus 60.0 s
|
no data
|
|
Estimated Stiffness Modulus 60.0 s
|
238 MPa
|
|
Difference between stiffness moduli 60.0 s
|
no data
|
|
Estimated m-value 60.0 s
|
0.306
|
DIME Test ID: 2025-05-22-51-5
Test Method: AASHTO T51-22: Standard Method of Test for Ductility of Asphalt Materials (Asphalt Binder)
Verified Date: 06/25/2025
Date Tested: 06/25/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: Ductility
Test Result Compliance: complies
Additional Comments When Verified:
|
Is a normal test obtainable?
|
Yes
|
|
Number of replicates tested
|
Three
|
|
Ductility of test #1 (D1)
|
150 cm
|
|
Ductility of test #2 (D2)
|
150 cm
|
|
Ductility of test #3 (D3)
|
150 cm
|
|
Ductility of sample
|
150 cm
|
DIME Test ID: 2025-05-22-51-6
Test Method: AASHTO T316-22: Standard Method of Test for Viscosity Determination of Asphalt Binder Using Rotational Viscometer
Verified Date: 06/25/2025
Date Tested: 06/13/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: Viscosity @135C
Test Result Compliance: complies
Additional Comments When Verified:
|
Is viscosity reading in cP/Pa-s?
|
cP
|
|
Time of test
|
00:00 HH:MM
|
|
Test Temperature
|
134.9 C
|
|
Speed
|
20 rpm
|
|
Spindle size
|
.463 in
|
|
Torque
|
12.2 %
|
|
Viscosity reading #1 (A)
|
304.8 cP
|
|
Viscosity reading #2 (B)
|
305.1 cP
|
|
Viscosity reading #3 (C)
|
305.1 cP
|
|
Average viscosity
|
0.305 Pa-s
|
DIME Test ID: 2025-05-22-51-8
Test Method: AASHTO T240-23: Standard Method of Test for Effect of Heat and Air on a Moving Film of Asphalt Binder (Rolling Thin-Film Oven Test)
Verified Date: 06/25/2025
Date Tested: 06/13/2025
Submitted By Organization: Atlas - Denver
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: ian.broddrick@dot.ca.gov
Organization Phone: (916) 741-2680
General Comments for this Test: Mass Change
Test Result Compliance: complies
Additional Comments When Verified:
|
Is mass change based on one or two containers?
|
Two
|
|
Is mass change correction factor needed?
|
Yes
|
|
Any material loss from containers during heating process/testing?
|
No
|
|
Mass of container #1 before test (m1i)
|
205.625 grams
|
|
Mass of container #2 before test (m2i)
|
209.159 grams
|
|
Mass of container #1 after test (m1f)
|
205.408 grams
|
|
Mass of container #2 after test (m2f)
|
208.947 grams
|
|
Average mass change
|
-0.584 percent
|
|
Mass of empty container #1
|
170.554 grams
|
|
Mass of empty container #2
|
174.357 grams
|
|
Mass correction factor
|
0.03
|