Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 88888 DEA: SMTL-STOCK EFIS: SMTL-STOCK
QA Service Level:
DIST-CO-RTE-PM: 59---
Work Description: Special project for SMTL stock material. Object Code: 1025. J2 DEA: 912680.
Location Description:
Contractor Name: Unknown
Contractor Address: Unknown
Resident Engineer: Unknown Structure Rep.: Unknown
DIME Sample ID: 2025-04-24-17
TL Number from the TL Form:
Sample Submitted By Organization: CT HQ - Sacramento Structural Materials Testing Laboratory
Sample Organization Contact: (530) 329-6527
Type of Sample: Quality Assurance
Type of Material: SMTL TM6 - Ductile Iron Cast Samples
Sample Taken Date: 04/24/2025
Date that the sample was received by the laboratory/organization performing the testing: 04/28/2025
The quantity of what the sample constitutes: 2
A brief description of the sample: Ductile Iron Castings
From where was the sample collected: Manufacturer
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: SDI
Heat Number (s): H303, C214
Part Number (s): SDI 12 6 AH SDI 27 6 AH
Material Specification: A536
Grades: 80-55-06
Metal Foundry Manufacturer (Mill): Farrar Corporation
Prestressing Manufacturer: SDI
DIME Test ID: 2025-04-24-17-1
Test Method: ASTM A370-20: Standard Test Methods and Definitions for Mechanical Testing of Steel Products (Tensile - Round Sample)
Verified Date: 06/05/2025
Date Tested: 06/03/2025
Submitted By Organization: Atlas - Oakland
Organization Address: 534 23rd Avenue,
Organization City: Oakland
Organization State: CA
Organization Zipcode: 94606
Organization Email: guillermo.baltazar@oneatlas.com
Organization Phone: (510) 434-3018
General Comments for this Test:
Test Result Compliance:
Additional Comments When Verified:
|
Number of Samples
|
2
|
| Sample | Heat Number | Diameter (in) | Area (sqin) | Stress at Offset (psi) | Tensile Strength (psi) | Elongation in 4 x d (%) | Tested By | | 1A | H303 | 0.505 | 0.2003 | 66100 | 107500 | 6.2 | Miguel Baltaza | | 2A | C214 | 0.505 | 0.2003 | 63100 | 109000 | 6.4 | Miguel Baltaza |
| |
|
UTM
|
NA
|
|
Temperature
|
72 f
|