Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 1000189 DEA: 112N1714 EFIS: 1122000284
QA Service Level: 1
DIST-CO-RTE-PM: 11-SD-805-0.5/14.6
Work Description: METHACRYLATE REPLACE APPROACH SLABS, JOINT SEALS AND CONCRETE OVERLAY.
Location Description: SAN DIEGO COUNTY AT VARIOUS LOCATIONS FROM SOUTH ROUTE 805/5 SEPARATION TO ROUTE 805/15 SEPARATION
Contractor Name: PETERSON-CHASE GENERAL ENGINEERING CONSTRUCTION, INC.
Contractor Address: 16351 CONSTRUCTION CIR W, IRVINE CA 92606
Resident Engineer: John Tran Structure Rep.: Unknown
DIME Sample ID: 2025-04-16-42
TL Number from the TL Form: Sacramento Caltrans lab
Sample Submitted By Organization: Kwik Bond Polymers
Sample Organization Contact: (760) 518-6064
Type of Sample: Quality Control
Type of Material: Polyester
Sample Taken Date: 04/16/2025
Date that the sample was received by the laboratory/organization performing the testing: 04/17/2025
The quantity of what the sample constitutes: 17 totes
A brief description of the sample: 1 gallon can / PPC 1121 Resin
From where was the sample collected: Source
Laboratory sample identification: 000156KBP
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Kwik Bond Polymers, Benicia
DIME Test ID: 2025-04-16-42-1
Test Method: ASTM D2196-Feb15: Standard Test Methods for Rheological Properties of Non-Newtonian Materials by Rotational Viscometer
Verified Date: 06/18/2025
Date Tested: 06/17/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
DIME Test ID: 2025-04-16-42-2
Test Method: ASTM D1475-Nov13: Standard Test Method For Density of Liquid Coatings, Inks, and Related Products
Verified Date: 06/18/2025
Date Tested: 06/17/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
|
Density Units
|
pounds/gallons
|
|
Liquid Density (pounds per gallon)
|
9
|
DIME Test ID: 2025-04-16-42-3
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Verified Date: 06/18/2025
Date Tested: 06/17/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
|
Number of specimens tested
|
6
|
|
Conditioning procedure
|
18/25/50+5/70
|
|
Speed of testing
|
0.45 in/min
|
|
Sample 1 Width
|
0.517 in
|
|
Sample 1 Ultimate strength
|
2791.1 psi
|
|
Sample 1 Thickness
|
0.226 in
|
|
Sample 1 Area
|
0.1168 in^2
|
|
Sample 1 Ultimate Strength Actual
|
326 lbs
|
|
Sample 1 percent elongation
|
49 %
|
|
Sample 1 Time
|
no data0 MM:SS
|
|
Sample 2 Width
|
0.515 in
|
|
Sample 2 Thickness
|
0.22 in
|
|
Sample 2 Area
|
0.1133 in^2
|
|
Sample 2 Ultimate strength
|
2992.1 psi
|
|
Sample 2 Ultimate Strength Actual
|
339 lbs
|
|
Sample 2 percent elongation
|
59 %
|
|
Sample 2 Time
|
no data0 MM:SS
|
|
Sample 3 Width
|
0.516 in
|
|
Sample 3 Thickness
|
0.258 in
|
|
Sample 3 Area
|
0.1331 in^2
|
|
Sample 3 Ultimate strength
|
2712.2 psi
|
|
Sample 3 Ultimate Strength Actual
|
361 lbs
|
|
Sample 3 percent elongation
|
48 %
|
|
Sample 3 Time
|
no data0 MM:SS
|
|
Sample 4 Width
|
0.513 in
|
|
Sample 4 Thickness
|
0.225 in
|
|
Sample 4 Area
|
0.1154 in^2
|
|
Sample 4 Ultimate strength
|
2790.3 psi
|
|
Sample 4 Ultimate Strength Actual
|
322 lbs
|
|
Sample 4 percent elongation
|
53 %
|
|
Sample 4 Time
|
no data0 MM:SS
|
|
Sample 5 Width
|
0.52 in
|
|
Sample 5 Thickness
|
0.262 in
|
|
Sample 5 Area
|
0.1362 in^2
|
|
Sample 5 Ultimate strength
|
2797.4 psi
|
|
Sample 5 Ultimate Strength Actual
|
381 lbs
|
|
Sample 5 percent elongation
|
56 %
|
|
Sample 5 Time
|
no data0 MM:SS
|
|
Sample 6 Width
|
0.519 in
|
|
Sample 6 Thickness
|
0.239 in
|
|
Sample 6 Area
|
0.124 in^2
|
|
Sample 6 Ultimate strength
|
2887.1 psi
|
|
Sample 6 Ultimate Strength Actual
|
358 lbs
|
|
Sample 6 percent elongation
|
55 %
|
|
Sample 6 Time
|
no data0 MM:SS
|
|
Ultimate Strength Average
|
2828 psi
|
|
Percent Elongation Average
|
53 %
|
DIME Test ID: 2025-04-16-42-4
Test Method: CTM 551-August 2012: Method of Test for Determining Suitability of Materials for Overlayment and Repair of Portland Cement Concrete Pavements and Structures
Verified Date: 06/18/2025
Date Tested: 04/23/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test: Accepted supplier's result.
Test Result Compliance: complies
Additional Comments When Verified:
|
Curing history for Sample 1
|
24hr
|
|
Maximum applied load (P) for Sample 1
|
1404 lb
|
|
Span length for Sample 1
|
9 in
|
|
Break location for Sample 1
|
bond
|
|
Specimen defects/notes for Sample 1
|
no data
|
|
Surface type for Sample 1
|
SSD
|
|
Modulus of rupture (R) for Sample 1
|
702 psi
|
|
Curing history for Sample 2
|
24hr
|
|
Maximum applied load (P) for Sample 2
|
1258 lb
|
|
Span length for Sample 2
|
9 in
|
|
Break location for Sample 2
|
bond
|
|
Specimen defects/notes for Sample 2
|
no data
|
|
Surface type for Sample 2
|
SSD
|
|
Modulus of rupture (R) for Sample 2
|
629 psi
|
|
Curing history for Sample 3
|
24hr
|
|
Maximum applied load (P) for Sample 3
|
1626 lb
|
|
Span length for Sample 3
|
9 in
|
|
Break location for Sample 3
|
bond
|
|
Specimen defects/notes for Sample 3
|
no data
|
|
Surface type for Sample 3
|
SSD
|
|
Modulus of rupture (R) for Sample 3
|
813 psi
|
DIME Test ID: 2025-04-16-42-5
Test Method: SCAQMD 309-91-Feb93: Determination of Static Volatile Emissions
Verified Date: 06/18/2025
Date Tested: 06/17/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
|
Diameter of lid
|
153.79 mm
|
|
Room Temperature
|
74 f
|
|
Tare weight
|
no data
|
|
Initial weight
|
100.07 grams
|
|
Weight at 5 minutes
|
99.9 grams
|
|
Weight at 10 minutes
|
99.77 grams
|
|
Weight at 15 minutes
|
99.64 grams
|
|
Weight at 20 minutes
|
99.51 grams
|
|
Weight at 25 minutes
|
99.38 grams
|
|
Weight at 30 minutes
|
99.26 grams
|
|
Final weight
|
99.26 grams
|
|
Total weight loss
|
0.81 grams
|
|
Calculated radius of gallon can lid in cm
|
7.69 cm
|
|
Lid Factor
|
53.827 m^2
|
|
Volatile emission
|
43.6 grams/m^2
|
DIME Test ID: 2025-04-16-42-6
Test Method: ASTM D2369-Jul10: Standard Test Method for Volatile Content of Coatings
Verified Date: 06/18/2025
Date Tested: 06/17/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
|
Mean of two volatile content determination
|
45
|