Print Report | Back to Sample Detail

Sample Record for 2025-03-12-6

Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.

Project Information

Project ID: 212861 DEA: 101H2804 EFIS: 1017000190 QA Service Level: 1
DIST-CO-RTE-PM: 10-STA-5-10.7/25.5
Work Description: BRIDGE DECK OVERLAY WITH POLYESTER CONCRETE, REPLACE APPROACH SLABS & JOINT SEALS IN STANISLAUS COUNTY ON STATE ROUTE 5 FROM FINK ROAD UC TO KHALSA ROAD UC.
Location Description: STANISLAUS AND MERCED COUNTIES.
Contractor Name: MYERS & SONS CONSTRUCTION, LLC
Contractor Address: 45 Morrison Avenue, Sacramento, CA 95838
Resident Engineer: Zubair Anwar Structure Rep.: Sai Kasaraneni

Sample Information

DIME Sample ID: 2025-03-12-6
TL Number from the TL Form: Sacramento Caltrans lab
Sample Submitted By Organization: Kwik Bond Polymers
Sample Organization Contact: (760) 518-6064
Type of Sample: Quality Control
Type of Material: Polyester
Sample Taken Date: 03/12/2025
Date that the sample was received by the laboratory/organization performing the testing: 03/14/2025
The quantity of what the sample constitutes: 10 Tankers
A brief description of the sample: 1 gallon can / PPC 1121 RESIN
From where was the sample collected: Source
Laboratory sample identification: 000154KBP
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Kwik Bond Polymers, Benicia

Material Information

Mfg. Lot Number(s): AZ5B00278S
Batch number: AZ5B00278S
Mix number: AZ5B00278S
Test results on following page(s): 5

Test Results

Test 1 of 5

DIME Test ID: 2025-03-12-6-1
Test Method: ASTM D2196-Feb15: Standard Test Methods for Rheological Properties of Non-Newtonian Materials by Rotational Viscometer
Verified Date: 04/29/2025
Date Tested: 04/23/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Viscosity 83.5

Test 2 of 5

DIME Test ID: 2025-03-12-6-2
Test Method: ASTM D1475-Nov13: Standard Test Method For Density of Liquid Coatings, Inks, and Related Products
Verified Date: 04/29/2025
Date Tested: 04/23/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Density Units pounds/gallons
Liquid Density (pounds per gallon) 9

Test 3 of 5

DIME Test ID: 2025-03-12-6-3
Test Method: ASTM D638-Dec14: Standard Test Method for Tensile Properties of Plastics
Verified Date: 04/29/2025
Date Tested: 04/11/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Number of specimens tested 6
Conditioning procedure 18/25/50+5/70
Speed of testing 0.45 in/min
Sample 1 Width 0.522 in
Sample 1 Ultimate strength 2872.8 psi
Sample 1 Thickness 0.244 in
Sample 1 Area 0.1274 in^2
Sample 1 Ultimate Strength Actual 366 lbs
Sample 1 percent elongation 65 %
Sample 1 Time no data0 MM:SS
Sample 2 Width 0.519 in
Sample 2 Thickness 0.245 in
Sample 2 Area 0.1272 in^2
Sample 2 Ultimate strength 2838.1 psi
Sample 2 Ultimate Strength Actual 361 lbs
Sample 2 percent elongation 62 %
Sample 2 Time no data0 MM:SS
Sample 3 Width 0.503 in
Sample 3 Thickness 0.244 in
Sample 3 Area 0.1227 in^2
Sample 3 Ultimate strength 2844.3 psi
Sample 3 Ultimate Strength Actual 349 lbs
Sample 3 percent elongation 62 %
Sample 3 Time no data0 MM:SS
Sample 4 Width 0.505 in
Sample 4 Thickness 0.246 in
Sample 4 Area 0.1242 in^2
Sample 4 Ultimate strength 2938.8 psi
Sample 4 Ultimate Strength Actual 365 lbs
Sample 4 percent elongation 65 %
Sample 4 Time no data0 MM:SS
Sample 5 Width 0.514 in
Sample 5 Thickness 0.243 in
Sample 5 Area 0.1249 in^2
Sample 5 Ultimate strength 2834.3 psi
Sample 5 Ultimate Strength Actual 354 lbs
Sample 5 percent elongation 61 %
Sample 5 Time no data0 MM:SS
Sample 6 Width 0.505 in
Sample 6 Thickness 0.251 in
Sample 6 Area 0.1268 in^2
Sample 6 Ultimate strength 2862.8 psi
Sample 6 Ultimate Strength Actual 363 lbs
Sample 6 percent elongation 64 %
Sample 6 Time no data0 MM:SS
Ultimate Strength Average 2865 psi
Percent Elongation Average 63 %

Test 4 of 5

DIME Test ID: 2025-03-12-6-4
Test Method: ASTM D2369-Jul10: Standard Test Method for Volatile Content of Coatings
Verified Date: 04/29/2025
Date Tested: 04/23/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Mean of two volatile content determination 46

Test 5 of 5

DIME Test ID: 2025-03-12-6-5
Test Method: SCAQMD 309-91-Feb93: Determination of Static Volatile Emissions
Verified Date: 04/29/2025
Date Tested: 04/23/2025
Submitted By Organization: Future Labs, LLC
Organization Address: 124 Lone Wolf Drive,
Organization City: Madison
Organization State: MS
Organization Zipcode: 39110
Organization Email: alexh@futurelabsllc.com
Organization Phone:
General Comments for this Test:
Test Result Compliance: complies
Additional Comments When Verified:
Diameter of lid 154.11 mm
Room Temperature 75 f
Tare weight no data
Initial weight 100.21 grams
Weight at 5 minutes 100.04 grams
Weight at 10 minutes 99.89 grams
Weight at 15 minutes 99.75 grams
Weight at 20 minutes 99.61 grams
Weight at 25 minutes 99.47 grams
Weight at 30 minutes 99.32 grams
Final weight 99.32 grams
Total weight loss 0.89 grams
Calculated radius of gallon can lid in cm 7.706 cm
Lid Factor 53.603 m^2
Volatile emission 47.707 grams/m^2