Note: Fields with no data or with a value of "Unknown" will not be displayed on the print out.
Project ID: 995055 DEA: 024H0504 EFIS: 0218000080
QA Service Level: 1
DIST-CO-RTE-PM: 02-SHA-273,299-18.5/18.7,24.1/30.3
Work Description: PLACE RHMA, HMA, MINOR CONCRETE, AND REPLACE AC SURFACING.
Location Description: SHASTA COUNTY IN AND NEAR REDDING ON ROUTE 273 FROM 0.5 MILE NORTH OF SULPHUR CREEK BRIDGE TO 0.2 MILE SOUTH OF TWIN VIEW BOULEVARD AND ON ROUTE 299 FROM 0.2 MILE WEST OF HILLTOP DRIVE TO 0.1 MILE EAST OF HOOTENANNY LANE
Contractor Name: TULLIS, INC.
Contractor Address: 16951 Clear Creek Road, Redding, CA 96001
Resident Engineer: Nathan Alexander Structure Rep.: Nicolas Jimenez
DIME Sample ID: 2024-10-07-70
TL Number from the TL Form: 858520
Sample Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Sample Organization Contact: (916) 227-7302
Type of Sample: Production Start-Up
Type of Material: Asphalt Binder
Sample Taken Date: 10/07/2024
Date that the sample was received by the laboratory/organization performing the testing: 10/22/2024
The quantity of what the sample constitutes: 2 CAN
A brief description of the sample: BINDER
From where was the sample collected: Source
Laboratory sample identification:
Structure unique identifier:
Structure name:
The fabricator/manufacturer/facility name: Valero - Benicia, CA
Performance Grade: PG 58-22
Modified: No
Lot number: 1
Sublot number: 1
Tank number:
Time of sample:
HMA Supplier: Tullis North state Asphalt
Certified Asphalt Supplier: Valero Marketing & Supply - Benicia CA
Multigrade: No
Multigrade Type:
Asphalt Binder Mix Number:
DIME Test ID: 2024-10-07-70-1
Test Method: AASHTO T315-22: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 01/16/2025
Date Tested: 12/20/2024
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (530) 713-6823
General Comments for this Test: ORIGINAL
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
Original binder
|
|
Test Gap
|
1 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
12.06 %
|
|
Stress Amplitude
|
0.229 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
87.1 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
1.897 kPa
|
|
Test Temperature (Specimen 1)
|
58.0 C
|
|
Dynamic Shear, G*/sin(δ)
|
1.90 kPa
|
DIME Test ID: 2024-10-07-70-2
Test Method: AASHTO T315-22: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 01/16/2025
Date Tested: 12/20/2024
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (530) 713-6823
General Comments for this Test: RTFO
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
RTFO residue
|
|
Test Gap
|
1 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
10.05 %
|
|
Stress Amplitude
|
0.425 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
84.1 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
4.225 kPa
|
|
Test Temperature (Specimen 1)
|
58.0 C
|
|
Dynamic Shear, G*/sin(δ)
|
4.25 kPa
|
DIME Test ID: 2024-10-07-70-3
Test Method: AASHTO T315-22: Standard Method of Test for Determining the Rheological Properties of Asphalt Binder Using a Dynamic Shear Rheometer (DSR) (Dynamic Shear)
Verified Date: 01/16/2025
Date Tested: 12/28/2024
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (530) 713-6823
General Comments for this Test: PAV
Test Result Compliance: complies
Additional Comments When Verified:
|
Phase
|
PAV residue
|
|
Test Plate Diameter
|
8 mm
|
|
Test Gap
|
2 mm
|
|
Test Frequency
|
10.0 rad/s
|
|
Strain Amplitude
|
1.01 %
|
|
Stress Amplitude
|
63.040 kPa
|
|
Phase Angle (δ) (for the 10 cycles)
|
51.6 degree
|
|
Complex Modulus (G*) (for the 10 measurements)
|
6272.422 kPa
|
|
Test Temperature (Specimen 1)
|
22.0 C
|
|
(G*) x sin(δ)=
|
4916 kPa
|
DIME Test ID: 2024-10-07-70-4
Test Method: AASHTO T51-22: Standard Method of Test for Ductility of Asphalt Materials (Asphalt Binder)
Verified Date: 01/16/2025
Date Tested: 12/20/2024
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (530) 713-6823
General Comments for this Test: DUCTILITY
Test Result Compliance: complies
Additional Comments When Verified:
|
Is a normal test obtainable?
|
Yes
|
|
Number of replicates tested
|
One
|
|
Ductility of test #1 (D1)
|
84 cm
|
|
Ductility of sample
|
84 cm
|
DIME Test ID: 2024-10-07-70-5
Test Method: AASHTO T313-22: Standard Method of Test for Determining the Flexural Creep Stiffness of Asphalt Binder Using the Bending Beam Rheometer (BBR)
Verified Date: 01/16/2025
Date Tested: 12/20/2024
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (530) 713-6823
General Comments for this Test: BBR
Test Result Compliance: complies
Additional Comments When Verified:
|
Time test started
|
no data HH:MM:SS
|
|
Flags issued by software during test
|
no data
|
|
Correlation coefficient (R²)
|
no data0
|
|
Regression coefficient a
|
no data
|
|
Regression coefficient b
|
no data
|
|
Regression coefficient c
|
no data
|
|
Load at time 0.0
|
no data0 mN
|
|
Deflection at time 0.0 s
|
no data0 µm
|
|
Load at time 0.5 s
|
no data0 mN
|
|
Deflection at time 0.5 s
|
no data0 µm
|
|
Load at 60.0 s
|
no data0 mN
|
|
Beam deflection 60.0 s
|
no data0 µm
|
|
Measured Stiffness Modulus 60.0 s
|
214 MPa
|
|
Estimated Stiffness Modulus 60.0 s
|
no data
|
|
Difference between stiffness moduli 60.0 s
|
no data
|
|
Estimated m-value 60.0 s
|
0.343
|
DIME Test ID: 2024-10-07-70-8
Test Method: AASHTO T44-18: Standard Method of Test for Solubility of Bituminous Materials
Verified Date: 01/16/2025
Date Tested: 12/20/2024
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (530) 713-6823
General Comments for this Test: SOLUBILITY
Test Result Compliance: complies
Additional Comments When Verified:
|
Was test performed on residue from distillation or evaporation?
|
Evaporation
|
|
Soluble, percent
|
99.9 %
|
|
Insoluble, percent
|
0.1 %
|
DIME Test ID: 2024-10-07-70-9
Test Method: AASHTO T316-17: Standard Method of Test for Viscosity Determination of Asphalt Binder Using Rotational Viscometer
Verified Date: 01/16/2025
Date Tested: 12/20/2024
Submitted By Organization: CT HQ - Sacramento Asphalt Binder Laboratory
Organization Address: 5900 Folsom Boulevard,
Organization City: Sacramento
Organization State: CA
Organization Zipcode: 95819
Organization Email: guadalupe.magana@dot.ca.gov
Organization Phone: (530) 713-6823
General Comments for this Test: VISC
Test Result Compliance: complies
Additional Comments When Verified:
|
Is viscosity reading in cP/Pa-s?
|
Pa-s
|
|
Time of test
|
00:00 HH:MM
|
|
Test Temperature
|
135 C
|
|
Speed
|
20 rpm
|
|
Spindle size
|
0.66 in
|
|
Torque
|
11.3 %
|
|
Viscosity reading #1 (A)
|
0.283 Pa-s
|
|
Viscosity reading #2 (B)
|
0.283 Pa-s
|
|
Viscosity reading #3 (C)
|
0.283 Pa-s
|
|
Average viscosity
|
0.283 Pa-s
|